Glass Expert Performs a Failure Analysis on a Broken Wine Bottle



Read Consulting glass experts performed a failure analysis on a broken wine bottle. The failure analysis determined that the side of the cork screw had exited the cork and created glass damage that initiated a failure when the cork was being removed. The side of the cork screw crushed the interior wall of the bottle neck. 

PVC Plastic Pipe Failure Analysis



 Read Consulting a California failure analysis lab often performs plastic failure analysis. The failure analysis laboratory was asked to look a a broken 3" diameter PVC pipe. In this case, the plastic plumbing broke due to bending overload. At the origin the failure started as overload the white portion at the origin (see the 10 X micro graph). Under load the crack grew to a length that then turned into brittle failure.